Enhanced TDS
Identification & Functionality
- Chemical Family
- RTU Product Type
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
- Product Features
- High reactivity system for composite parts
Applications & Uses
- Composites Processing Methods
- Product End Uses
Technical Details & Test Data
- Processing Guidelines
- Wet lay-up
- Resin Transfer Moulding
- Properties of The Cured, Neat Formulation
Property Value Unit Test Method At Condition Glass Transition Temperature 50 - 58 °C ISO 11357-2, DSC 1d 23°C Glass Transition Temperature 55 - 63 °C ISO 11357-2, DSC 3d 23°C Glass Transition Temperature 58 - 66 °C ISO 11357-2, DSC 7d 23°C Glass Transition Temperature 60 - 69 °C ISO 11357-2, DSC 3h 40°C Glass Transition Temperature 65 - 73 °C ISO 11357-2, DSC 2h 50°C Glass Transition Temperature 70 - 78 °C ISO 11357-2, DSC 1h 60°C Glass Transition Temperature 79 - 86 °C ISO 11357-2, DSC 15min 80°C Glass Transition Temperature 88 - 96 °C ISO 11357-2, DSC 1h 80°C Glass Transition Temperature 90 - 98 °C ISO 11357-2, DSC 3min 100°C Glass Transition Temperature 90 - 98 °C ISO 11357-2, DSC 10min 100°C Glass Transition Temperature 90 - 98 °C ISO 11357-2, DSC 10min 80°C + 20min 100°C
Glass Transition Temperature 95 - 105 °C ISO 11357-2, DSC 10min 80°C + 20min 120°C
Glass Transition Temperature 96 - 106 °C ISO 11357-2, DSC 10min 80°C + 20min 130°C
Flexural Test 130 - 145 MPa ISO 178 7d 23°C Flexural Test 3 - 5 % ISO 178 7d 23°C Flexural Test 125 - 135 MPa ISO 178 7d 23°C Flexural Test 4 - 7 % ISO 178 7d 23°C Flexural Test 3750 - 3950 MPa ISO 178 7d 23°C Flexural Test 145 - 155 MPa ISO 178 7d 23°C Flexural Test 4 - 6 % ISO 178 7d 23°C Flexural Test 120 - 130 MPa ISO 178 7d 23°C Flexural Test 5 - 7 % ISO 178 7d 23°C Flexural Test 3650 - 3850 MPa ISO 178 7d 23°C Fracture Properties 0.75 - 1.05 MPa√m ISO 13586 7d 23°C Fracture Properties 160 - 200 J/m² ISO 13586 7d 23°C Fracture Properties 0.70 - 1.00 MPa√m ISO 13586 7d 23°C Fracture Properties 130 - 150 J/m² ISO 13586 7d 23°C Water Absorption 0.18 - 0.22 % Not specified 7d 23°C Water Absorption 0.60 - 0.65 % Not specified 7d 23°C Water Absorption 0.12 - 0.16 % Not specified 7d 23°C Water Absorption 0.45 - 0.50 % Not specified 7d 23°C Flexural Test 125 - 140 MPa ISO 178 10min 80°C + 20min 100°C
Flexural Test 5 - 6 % ISO 178 10min 80°C + 20min 100°C
Flexural Test 85 - 100 MPa ISO 178 10min 80°C + 20min 100°C
Flexural Test 6.5 - 9.0 % ISO 178 10min 80°C + 20min 100°C
Flexural Test 3150 - 3350 MPa ISO 178 10min 80°C + 20min 100°C
Flexural Test 120 - 140 MPa ISO 178 10min 80°C + 20min 100°C
Flexural Test 5 - 6 % ISO 178 10min 80°C + 20min 100°C
Flexural Test 85 - 100 MPa ISO 178 10min 80°C + 20min 100°C
Flexural Test 5 - 7 % ISO 178 10min 80°C + 20min 100°C
Flexural Test 3200 - 3500 MPa ISO 178 10min 80°C + 20min 100°C
Water Absorption 0.13 - 0.18 % Not specified 10min 80°C + 20min 100°C
Water Absorption 0.37 - 0.42 % Not specified 10min 80°C + 20min 100°C
Water Absorption 0.12 - 0.16 % Not specified 10min 80°C + 20min 100°C
Water Absorption 0.35 - 0.40 % Not specified 10min 80°C + 20min 100°C
Fracture toughness K1C 1.20 - 1.50 MPa√m ISO 13586 10min 80°C + 20min 100°C
Fracture energy G1C 420 - 520 J/m² ISO 13586 10min 80°C + 20min 100°C
Fracture toughness K1C 1.05 - 1.20 MPa√m ISO 13586 10min 80°C + 20min 100°C
Fracture energy G1C 280 - 325 J/m² ISO 13586 10min 80°C + 20min 100°C
Safety & Health
- First Aid Information
- Contamination of the eyes by resin, hardener or mix should be treated immediately by flushing with clean, running water for 10 to 15 minutes.
- A doctor should then be consulted. Material smeared or splashed on the skin should be dabbed off, and the contaminated area then washed and treated with a cleansing cream (see above).
- A doctor should be consulted in the event of severe irritation or burns.
- Contaminated clothing should be changed immediately. Anyone taken ill after inhaling vapours should be moved out of doors immediately. In all cases of doubt call for medical assistance.
Storage & Handling
- Storage Conditions
- Provided that Araldite® LY 1564, Araldite® LY 3585 or Hardener XB 3458 are stored in a dry place in their original, properly closed containers at the storage temperatures mentioned in the MSDS they will have the shelf lives indicated on the labels.
- Partly emptied containers should be closed immediately after use.
- Araldite® LY 3585 which has crystallized and looks cloudy can be restored to its original state by heating to 60 - 80°C.
- Handling Information
Safety Precautions Protective clothing Yes Gloves Essential Arm protectors Recommended when skin contact likely
Goggles/safety glasses Yes Respirator/dust mask Recommended Skin Protection Skin protection before starting Apply barrier cream to exposed skin
Skin protection after washing Apply barrier or nourishing cream
Cleansing of contaminated skin Dab off with absorbent paper, wash with warm water and alkali-free soap, then dry with disposable towels. Do not use solvents
Clean shop requirements Cover workbenches, etc. with light coloured paper. Use disposable breakers, etc.
Disposal of spillage Soak up with sawdust or cotton waste and deposit in plastic-lined bin
Ventilation Ventilation of workshop Renew air 3 to 5 times an hour
Ventilation of workplace Exhaust fans. Operatives should avoid inhaling vapours.