- Laminating Araldite® LY 3508 has a good toughness effect combined with a low viscosity
Applications & Uses
- Composites Processing Methods
- Product End Uses
- Processing Information
- Wet lay-up
- Filament Winding
- Pressure Moulding
- Resin Transfer Moulding (RTM)
Properties
- Physical Form
Technical Details & Test Data
- Processing Guidelines
Components Parts by weight Parts by volume Araldite® LY 3508 100 100 Aradur® 3486 30 37 - We recommend that the components are weighed with an accurate balance to prevent mixing inaccuracies which can affect the properties of the matrix system.
- The components should be mixed thoroughly to ensure homogeneity. It is important that the side and the bottom of the vessel are incorporated into the mixing process. When processing large quantities of mixture the pot life will decrease due to exothermic reaction.
- It is advisable to divide large mixes into several smaller containers.
- Properties of The Cured, Neat Formulation
Property ARALDITE® LY 3508 / ARADUR® 3486 Unit Test Method Condition Glass Transition Temperature (Tg) 68 - 74 °C ISO 11357-2, DSC, 10 K/MIN 16 h 50°C Glass Transition Temperature (Tg) 95 - 102 °C ISO 11357-2, DSC, 10 K/MIN 5 h 100°C Flexural Strength 110 - 125 MPa ISO 178 5 h 100°C Elongation at Flexural Strength 5.8 - 6.8 % ISO 178 5 h 100°C Ultimate Strength 90 - 100 MPa ISO 178 5 h 100°C Ultimate Elongation 10.0 - 12.5 % ISO 178 5 h 100°C Flexural Modulus 2750 - 2950 MPa ISO 178 5 h 100°C Fracture Toughness (K1C) 2.2 - 2.4 MPa√m ISO 13586 1 h 80°C + 8 h 140°C
Fracture Energy (G1C) 1500 - 1700 J/m² ISO 13586 1 h 80°C + 8 h 140°C
Water Absorption 0.48 - 0.55 % ISO 62 10 days H₂O 23°C
Safety & Health
- First Aid Information
- Contamination of the eyes by resin, hardener or mix should be treated immediately by flushing with clean, running water for 10 to 15 minutes.
- A doctor should then be consulted. Material smeared or splashed on the skin should be dabbed off, and the contaminated area then washed and treated with a cleansing cream (see above). A doctor should be consulted in the event of severe irritation or burns.
- Contaminated clothing should be changed immediately. Anyone taken ill after inhaling vapours should be moved out of doors immediately. In all cases of doubt call for medical assistance.
Storage & Handling
- Storage Conditions
- Provided that Araldite® LY 3508, Aradur® 3486 are stored in a dry place in their original, properly closed containers at the storage temperatures mentioned in the MSDS they will have the shelf lives indicated on the labels.
- Partly emptied containers should be closed immediately after use. Epoxy Resin XU 3508 which has crystallized and looks cloudy can be restored to its original state by heating to 60 - 80°C.
- Handling Information
Safety Precautions Protective clothing Yes Gloves Essential Arm protectors Recommended when skin contact likely
Goggles/safety glasses Yes Respirator/dust mask Recommended Skin Protection Skin protection before starting Apply barrier cream to exposed skin
Skin protection after washing Apply barrier or nourishing cream
Cleansing of contaminated skin Dab off with absorbent paper, wash with warm water and alkali-free soap, then dry with disposable towels. Do not use solvents
Clean shop requirements Cover workbenches, etc. with light coloured paper. Use disposable breakers, etc.
Disposal of spillage Soak up with sawdust or cotton waste and deposit in plastic-lined bin
Ventilation Ventilation of workshop Renew air 3 to 5 times an hour
Ventilation of workplace Exhaust fans. Operatives should avoid inhaling vapours.