Enhanced TDS
Identification & Functionality
- Chemical Family
- Function
- Syntactic Adhesive,Casting Resin
- RTU Product Type
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Product Features
- Key Features
- High temperature performance
- Long work life
- Product Features
- High temperature performance
- Long work life
Applications & Uses
- Product End Uses
- Markets
- Applications
- Processing Information
Material temperatures should be above 18°C (65°F) when mixing. Mix both components thoroughly for several minutes to insure complete and uniform mixing.
Parameter
Value
Work life, 100 g at 25°C 4 - 5 hours Typical cure cycles
Cure 1: 4 hours at 83°C Cure 2: 2 hours at 121°C
Regulatory & Compliance
- OEM Specifications
Technical Details & Test Data
- Processing Condition
Processing Data:
Parameter Value Work life, 100 g at 25°C 4 - 5 hours Typical cure cycles Cure 1: 4 hours at 83°C, or Cure 2: 2 hours at 121°C Material temperatures should be above 18°C (65°F) when mixing. Mix both components thoroughly for several minutes to insure complete and uniform mixing.
- Typical Physical Properties
Property Test Method Cure 1 Cure 2 Durometer hardness, Shore D ASTM D2240 93 93 Flexural strength, 25°C, ksi (MPa) ASTM D790 As cured 77.4 (534) 104.0 (717) After 2 hours boiling water, 25°C 52.1 (359) 68.6 (473) Flexural modulus, 25°C, ksi (MPa) ASTM D790 As cured 3,021 (20,827) 3,801 (26,206) After 2 hours boiling water, 25°C 2,771 (19,103) 3,481 (24,000) Compressive strength, 25°C, ksi (MPa) ASTM D695 As cured 61.4 (423) 71.9 (496) Tested at 149°C 2.0 (13.8) 3.4 (23.4) Compressive modulus, 25°C, ksi (MPa) ASTM D695 As cured 3,751 (25,862) 4,031 (27,793) Tested at 149°C 937 (6462) 1,360 (9379) Tensile lap shear, Al-Al, as cured, at 25°C, psi (MPa) ASTM D1002 - 1090 (7.5) - Technical Data
Typical physical properties:
Unless otherwise stated, the data were determined with typical production batches using standard test methods. They are typical values only, and do not constitute a product specification.
Property Conditions Test Method Cure 1 Cure 2 Durometer hardness, Shore D - ASTM D2240 93 93 Flexural strength, 25°C, ksi (MPa) As cured ASTM D790 77.4 (534) 104.0 (717) Flexural strength, 25°C, ksi (MPa) After 2 hours boiling water, 25°C ASTM D790 52.1 (359) 68.6 (473) Flexural modulus, 25°C, ksi (MPa) As cured ASTM D790 3,021 (20,827) 3,801 (26,206) Flexural modulus, 25°C, ksi (MPa) After 2 hours boiling water, 25°C ASTM D790 2,771 (19,103) 3,481 (24,000) Compressive strength, 25°C, ksi (MPa) As cured ASTM D695 61.4 (423) 71.9 (496) Compressive strength, 25°C, ksi (MPa) Tested at 149°C ASTM D695 2.0 (13.8) 3.4 (23.4) Compressive modulus, 25°C, ksi (MPa) As cured ASTM D695 3,751 (25,862) 4,031 (27,793) Compressive modulus, 25°C, ksi (MPa) Tested at 149°C ASTM D695 937 (6,462) 1,360 (9,379) Tensile lap shear, Al-Al, as cured, at 25C, psi (MPa)
- ASTM D1002 - 1090 (7.5)
Packaging & Availability
- Regional Availability
Storage & Handling
- Storage Conditions
- EPOCAST® 35 A Resin and Hardener 927 should be stored in a dry place in the original sealed containers at temperatures between 2°C and 8°C (36°F and 46°F). After use, tightly reseal containers.
- The products should not be exposed to direct sunlight.
- Storage Conditions
EPOCAST® 35 A/927 should be stored in a dry place in the original sealed containers at temperatures between 2°C and 8°C (36°F and 46°F). After use, tightly reseal containers. Under these storage conditions, and when supplied under Huntsman standard certification, the products have a shelf life of 1 year (from date of shipment). The products should not be exposed to direct sunlight.
Other
- Processing & Application Methods
- Application Information
Value Units Test Method / Conditions Mix Ratio 0.25 %(W) Hardener : Resin - Physical Properties
Value Units Test Method / Conditions Density 1.13 g/cm³ ASTM D792 at 25°C Viscosity 7000.0 cPs ASTM D2196 at 25°C