Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Polymer Name
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Markets
- Applications
- Product Applications
- Thick wall technical parts, thin wall technical parts and seals and gaskets.
Properties
- Physical Form
- Notes
¹- Injection molded parts to meet DIN & ASTM requirements. Parts tempered for 20 hrs at 100 °C prior to testing.
²- Extruded film cut to ASTM requirements. Parts at room temperature aged prior to testing.
Regulatory & Compliance
- Chemical Inventories
Technical Details & Test Data
- Material Preparation
IROGRAN® A 95 K 4977 is supplied pre-dried, however to ensure trouble-free processing it is preferable to dry before use. The recommended drying conditions are:
- 3 hours at 100-110°C in circulating air
- 3 hours at 80-90°C in dehumidified air
- Dew point: -30°C
Safety & Health
- Health and Safety Information
Before undertaking any trials with this product it is essential that all personnel are aware of the necessary precautions that must be taken.
Packaging & Availability
Storage & Handling
- Storage Information
- IROGRAN® A 95 K 4977 has a minimum expected shelf life of 12 months after shipment date.
Other
- Appearance
- Opaque rough cut granules
- Mechanical Properties
Value Units Test Method / Conditions Compression Set 30.0 % % ISO 815 at 100°C, 24h Compression Set 35.0 % % ISO 815 at 100°C, 70h Compression Set 15.0 % % ISO 815 at 23°C, 70 hr Compression Set 25.0 % % ISO 815 at 70°C, 24 hr Hardness 46.0 Shore D Shore D ISO 7619 after 3 seconds Tear Strength 110.0 N/mm N/mm ISO 34-1 Tensile Strength 55.0 MPa MPa DIN 53504 - Physical Properties
Value Units Test Method / Conditions Density 1.2 g/cm³ g/cm³ ISO 1183-1