MPC- series has been developed to outstand in demanding environments, which require superior level of mechanical and dynamic properties in a very wide range of temperatures. It fits well with many different tough and heavy duty applications like wheels, rollers or specific technical parts. “G” series is designed for improved abrasion resistance.
Technical Details & Test Data
- Casting Information
Hardness (ShA) MPC2010G RCH900 R143C Catalyst (%) Molds T (°C) Pot life (sec) Demolding (min) 95 100.00 0 10.40 0.2-0.4 105-115 180-240 15-45 The amount of main components is given on parts by weight.
* Pot life and demolding time are referred to the system with the suggested amount of catalyst, Tecnokat D5 can be used to adjust pot life and demolding time.- Post Curing Information
Do not allow excessive cooling of molded parts between demolding and post-curing.
Hardness (ShA) Temperature (°C) Time (hours) 95 110 16 For hardness above 93 ShA, two annealing steps are recommended to quickly reach the best performances; let the material cool down to room temperature in between the 2 post curing processes.
Packaging & Availability
- Regional Availability
- Packaging Information
- Materials are available in following packaging: 25, 50 or 200 kg
Storage & Handling
- Handling Information
- In order to allow complete melting, pre-heat materials at following conditions (melting times are referred to 200 kg drums,stored at 20°C)
Pre-heating temperature (°C) 75 Pre-heating time (hours) 16 - After pre-heating, make sure all materials are completely melted.
- Well mix melted material by drilling or rolling the drum
- Load materials to the machine immediately after mixing.
- Materials must be stored under nitrogen blanket after use.
Other
- Mechanical Properties
Value Units Test Method / Conditions Compression Set 22.0 % % ISO 815 at 23°C, 70 hr Hardness 48.0-52.0 Shore D Shore D ISO 7619-1 Tear Strength 70.0 kN/m kN/m ISO 34-1 90° with nick Tear Strength 110.0 kN/m kN/m ISO 34-1 90° without nick Tear Strength 125.0 kN/m kN/m ISO 34-1 crescent with nick Tensile Strength 55.0 N/mm² N/mm² ISO 37 - Physical Properties
Value Units Test Method / Conditions Density 1.17 g/cm³ g/cm³ ISO 2781 Viscosity1 500.0-1000.0 mPa.s mPa.s