TECNOTHANE® MPT106 has been developed to be an all-purpose system for high-demanding applications operating at low temperature, underwater, or under hydrolytic environments. It excels in elasticity and dynamic properties, with a good balance of mechanical properties. TECNOTHANE® MPT106 is particularly suited for coating applications by brush and roller.
Properties
- Physical Form
Regulatory & Compliance
Technical Details & Test Data
- Post Curing Information
Do not allow excessive cooling of molded parts between demolding and post-curing.
Hardness (ShA) Temperature (°C) Time (hours) 88 90 16 - Casting Information
Hardness (ShA) MPT106 RT140/A Catalyst (%) Molds T (°C) Pot life (sec) Demolding (min) 88 100.00 5.40 * 85–100 200–270 30–50 The amount of main components is given on parts by weight.
*Pot life and demolding time are referred to the system without catalyst, TecnoKat D5 can be used to adjust pot life and demolding time.
Packaging & Availability
- Regional Availability
- Packaging Information
- Materials are available in following packaging: 5, 10 or 15kg
Storage & Handling
- Handling Information
- In order to allow complete melting, pre-heat materials at following conditions (melting times are referred to 200 kg drums,stored at 20°C)
Pre-heating temperature (°C) 75 Pre-heating time (hours) 24 - After pre-heating, make sure all materials are completely melted.
- Well mix melted material by drilling or rolling the drum
- Load materials to the machine immediately after mixing.
- Materials must be stored under nitrogen blanket after use.
Other
- Appearance (SDS)
- Solid
- Color (SDS)
- White
- Odor (SDS)
- Characteristic
- Mechanical Properties
Value Units Test Method / Conditions Compression Set 17.0 % % ISO 815 at 23°C, 70 hr Hardness 36.0-40.0 Shore D Shore D Hardness 86.0-90.0 Shore A Shore A ISO 7619-1 Tear Strength 34.0 kN/m kN/m ISO 34-1 90° with nick Tear Strength 62.0 kN/m kN/m ISO 34-1 90° without nick Tear Strength 65.0 kN/m kN/m ISO 34-1 crescent with nick Tensile Strength 35.0 N/mm² N/mm² - Physical Properties
Value Units Test Method / Conditions Density 1.12 g/cm³ g/cm³ ISO 2781 Viscosity1 2000.0-3600.0 mPa.s mPa.s