When used with a suitable epoxy resin, ARADUR® 3951 Epoxy Curing Agent has the following characteristics:
- Made into water-dilutable low-VOC paint
- Good compatibility with zinc powder
- Suitable for primer or primer-to-top applications
- Long operating time
- Very good corrosion protection
Applications & Uses
- Coating End Applications
- Compatible Polymers & Resins
- Compatible Substrates & Surfaces
- Markets
- Applications
- Application Information
Suitable for water-based or high solid two-component epoxy primer or topcoat, two-component epoxy zinc-rich primer, and primer-surface integrated type Topcoat. For use in general industrial, marine and repair markets.
Properties
- Physical Form
- Mix Ratio
The weight ratio of Araldite® PZ3891 epoxy emulsion to Araldite 3951 epoxy curing agent is 100:30.
Regulatory & Compliance
- Chemical Inventories
Packaging & Availability
- Regional Availability
Storage & Handling
- Operational Precautions
Mandatory and recommended industrial hygiene procedures must be followed when handling and disposing of our products.
- Storage Information
ARADUR® 3951 Epoxy Curing Agent should be stored in a dry place (preferably in the original sealed container) at a temperature between 2 - 40°C (the temperature should not drop below 0°C). This product should not be stored in a place exposed to direct sunlight.
Other
- Appearance
- Brownish yellow liquid
- Color (SDS)
- Dark Amber
- Odor (SDS)
- Slight
- Application Information
Value Units Test Method / Conditions Mix Ratio 163.0 g/100g g/100g With Araldite® GY 6010 Liquid Epoxy Resin - Chemical Properties
Value Units Test Method / Conditions Amine Value 120.0-150.0 mg KOH/g mg KOH/g ISO 9702 - Physical Properties
Value Units Test Method / Conditions Density 1.0 g/cm³ g/cm³ ISO 1675 at 20°C Flash Point min. 49.0 °C °C Pensky-Martens Closed Cup (PMCC) Flash Point min. 49.0 °C °C ISO 2719 Viscosity 2000.0-5000.0 mPa.s mPa.s ISO 2555 at 25°C