- Low viscosity.
- Flexible castings.
- Good thermal shock resistance.
Applications & Uses
- Application Area
- Composites Processing Methods
- Product End Uses
- Markets
- Applications
- Processing Information
- Preparation CW 2245 contains fillers, which tend to settle over time. It is therefore recommended to carefully homogenize the complete contents of the container before use. In the storage vessels of the production equipment, the pre-filled products should be stirred up from time to time to avoid sedimentation and irregular metering.
- Mixing The casting mix is best prepared by heating the resin up to 40 – 50 °C before stirring in the hardener. Brief degassing of the mix under 5 – 10 mbar vacuum improves the mixture homogeneity and enhances the dielectric properties of the castings.
- Curing To determine whether cross-linking has been carried to completion and the final properties are optimal, it is necessary to carry out relevant measurements on the actual object or to measure the glass transition temperature. Different gel and cure cycles in the customer’s manufacturing process could lead to a different degree of cross-linking and thus a different glass transition temperature.
- Application Information
- Voltage regulators.
- Suppressor chokes.
- Proximity switches.
- Ferrite core transformers.
- Processing Methods
Casting; vacuum casting.
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Electrical Properties
Electrical Properties: at 23°C. Cured for 24h/RT + 6h/60°C.
Dielectric strength (2 mm specimen) 16 kV/mm IEC 60243-1 Dielectric loss factor (tan δ, 50Hz, 25°C) 4.9 % IEC 60250 Dielectric loss factor (tan δ, 50Hz, 40°C) 7.4 % IEC 60250 Dielectric loss factor (tan δ, 50Hz, 60°C) 12.3 % IEC 60250 Dielectric constant (εr, 50Hz, 25°C) 5 IEC 60250 Dielectric constant (εr, 50Hz, 40°C) 5.75 IEC 60250 Dielectric constant (εr, 50Hz, 60°C) 7.6 IEC 60250 Tracking resistance (CTI) >600 IEC 60112 Electrolytic corrosion A/1.2 IEC 60426 Volume resistivity (ρ, 25°C) 2x10¹⁴ Ω cm IEC 60093 Volume resistivity (ρ, 40°C) 4x10¹³ Ω cm IEC 60093 Volume resistivity (ρ, 60°C) 4x10¹¹ Ω cm IEC 60093 - Mechanical & Physical Properties
Mechanical and Physical Properties: at 23°C. Cured for 24h/RT + 6h/60°C.
Glass Transition Temperature 63 °C Specific Gravity 1.61 g/cm³ Tensile Modulus 5500 MPa Tensile Strength 36 MPa Elongation at Break 0.8 % Coefficient of Thermal expansion (Alpha 1 < Tg) 69 ppm/K Thermal Conductivity 0.67 W/mK Hardness 80 Shore D Flammability V-0 (6 mm) Water Absorption (1 day at 23°C) 0.17 % by wt. Water Absorption (30 min at 100°C) 0.23 % by wt.
Storage & Handling
- Storage Conditions
- Store the components in a dry place according to the storage conditions stated on the label in tightly sealed original containers.
- Under these conditions, the shelf life will correspond to the expiry date stated on the label.
- After this date, the product may be processed only after reanalysis.
- Partly emptied containers should be tightly closed immediately after use.
Other
- Application Information
Value Units Test Method / Conditions Mix Ratio 0.09 %(W) %(W) Hardener : Resin