Enhanced TDS
Identification & Functionality
- Chemical Family
- RTU Product Type
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
- Key Properties
- low viscosity
- very long pot-life
- high irradiation resistance
- good electrical properties
- best mechanical properties
Applications & Uses
- Composites Processing Methods
- Cure Method
- Product End Uses
- Processing Methods
Vacuum Pressure Impregnation (VPI – process)
- Application Information
Large coils for magnets and rotating machines
Properties
- Physical Form
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Cured Properties
Key Value Unit Test Method Test Condition Glass transition temperature 95 - 100 °C ISO 11357-2 Cure: 4h 80°C + 4h 120°C
Tensile strength 88 - 91 MPa ISO 527 Cure: 4h 80°C + 4h 120°C
Elongation at tensile strength 5.0 - 6.0 % ISO 527 Cure: 4h 80°C + 4h 120°C
Ultimate strength 87 - 94 MPa ISO 527 Cure: 4h 80°C + 4h 120°C
Ultimate elongation 5.5 - 6.5 % ISO 527 Cure: 4h 80°C + 4h 120°C
Tensile modulus 3100 - 3200 MPa ISO 527 Cure: 4h 80°C + 4h 120°C
Flexural strength at 23°C 150 - 162 MPa ISO 178 Cure: 4h 80°C + 4h 120°C
Elongation at flexural strength 6.5 - 7.0 % ISO 178 Cure: 4h 80°C + 4h 120°C
Ultimate strength 148 - 155 MPa ISO 178 Cure: 4h 80°C + 4h 120°C
Ultimate elongation 6.5 - 8.0 % ISO 178 Cure: 4h 80°C + 4h 120°C
Flexural modulus 3050 - 3200 MPa ISO 178 Cure: 4h 80°C + 4h 120°C
Fracture toughness K1C 0.57 - 0.60 MPa√m ISO 13586 Cure: 4h 80°C + 4h 120°C
Fracture energy G1C 110 - 120 J/m² ISO 13586 Cure: 4h 80°C + 4h 120°C
Water absorption after 1 day at 23°C 0.10 - 0.15 % by wt ISO 62 Cure: 4h 80°C + 4h 120°C
Water absorption after 10 days at 23°C 0.35 - 0.40 % by wt ISO 62 Cure: 4h 80°C + 4h 120°C
Water absorption after 60 min at 100°C 0.20 - 0.25 % by wt ISO 62 Cure: 4h 80°C + 4h 120°C
Breakdown strength 20 - 25 kV/mm IEC 60243-1 Cured for 4h 100°C + 10h 140°C
Tracking resistance > 600 - <1 CTI IEC 60112 Cured for 4h 100°C + 10h 140°C
Electrolytic corrosion A1 grade IEC 60426 Cured for 4h 100°C + 10h 140°C
Safety & Health
- Industrial Hygiene
Mandatory and recommended industrial hygiene procedures should be followed when-ever our products are being handled and processed. For additional information please consult the corresponding Safety Data Sheets and the brochure "Hygienic precautions for handling plastics products”.
- First Aid
Contamination of the eyes by resin, hardener or casting mix should be treated immediately by flushing with clean, running water for 10 to 15 minutes. A doctor should then be consulted. Material smeared or splashed on the skin should be dabbed off, and the contaminated area then washed and treated with a cleansing cream (see above). A doctor should be consulted in the event of severe irritation or burns. Contaminated clothing should be changed immediately.
Anyone taken ill after inhaling vapours should be moved out of doors immediately. In all cases of doubt call for medical assistance.
- Handling Precautions
Safety precautions at workplace:
protective clothing : yes
gloves : essential
arm protectors : recommended when skin contact likely
goggles/safety glasses : yes
respirator/dust mask : recommended
Skin protection
before starting work : Apply barrier cream to exposed skin
after washing : Apply barrier or nourishing cream
Cleaning of contaminated skin : Dab off with absorbent paper, wash with warm water and alkali-free soap, then dry with disposable towels. Do not use solvents
Clean shop requirements : Cover workbenches, etc. with light coloured paper. Use disposable beakers, etc.
Disposal of spillage : Soak up with sawdust or cotton waste and deposit in plastic-lined bin
Ventilation:
of workshop : Renew air 3 to 5 times an hour
of workplace : Exhaust fans. Operatives should avoid inhaling vapors.
Storage & Handling
- Storage Conditions
The components have to be stored in tightly sealed and dry original containers according to the storage conditions on the product label. Under these conditions, the shelf life will correspond to the expiration date stated on the label. After this date, the product may be processed only following reanalysis. Partly emptied containers should be closed tightly immediately after use.
For information on waste disposal and hazardous products of decomposition in the event of fire, refer to the Material Safety Data Sheets (MSDS) for these particular products.
Other
- Application Information
Value Units Test Method / Conditions Mix Ratio 0.0025 %(W) %(W) Accelerator : Resin Mix Ratio 0.82 %(W) %(W) Hardener : Resin