- Wet lay-up
- Filament Winding
- Pressure Moulding
- Resin Transfer Moulding (RTM)
- Pultrusion
Properties
- Notes
- 1 h 80 °C + 4 h 120 °C
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Processing Guidelines
Components Parts by weight Parts by volume Araldite® LY 1564 100 100 Aradur® 3474 26 32 - We recommend that the components are weighed with an accurate balance to prevent mixing inaccuracies which can affect the properties of the matrix system.
- The components should be mixed thoroughly to ensure homogeneity. It is important that the side and the bottom of the vessel are incorporated into the mixing process.
- When processing large quantities of mixture the pot life will decrease due to exothermic reaction. It is advisable to divide large mixes into several smaller containers.
- Properties of The Cured, Neat Formulation
Property Value Unit Test Method At Condition Glass Transition Temperature 115 - 120 °C ISO 11357-2, DSC 1 h 80°C + 4 h 120°C
Tensile Test Tensile strength 75 – 80 MPa ISO 527 1 h 80°C + 4 h 120°C
Tensile Test Ultimate elongation 5.0 – 6.5 % ISO 527 1 h 80°C + 4 h 120°C
Tensile Test Tensile modulus 2750 – 2900 MPa ISO 527 1 h 80°C + 4 h 120°C
Flexural Test Flexural strength 120 - 130 MPa ISO 178 1 h 80°C + 4 h 120°C
Flexural Test Ultimate elongation 8.0 – 9.0 % ISO 178 1 h 80°C + 4 h 120°C
Flexural Test Flexural modulus 2750 - 2900 MPa ISO 178 1 h 80°C + 4 h 120°C
Fracture Properties Fracture toughness K1C 0.70 - 0.90 MPa√m ISO 13586 1 h 80°C + 4 h 120°C
Fracture Properties Fracture energy G1C 200 - 240 J/m² ISO 13586 1 h 80°C + 4 h 120°C
Water Absorption 0.30 – 0.35 % ISO 62 1 h 80°C + 4 h 120°C, 3 days H₂O 23°C
Water Absorption 0.45 – 0.55 % ISO 62 1 h 80°C + 4 h 120°C, 7 days H₂O 23°C
Water Absorption 0.55 – 0.65 % ISO 62 1 h 80°C + 4 h 120°C, 10 days H₂O 23 °C
- Properties of The Cured, Reinforced Formulation
Property Value Unit Test Method Interlaminar Shear strength 58 - 62 MPa ASTM D 2344 Note
- Samples: 12 layers E-glass fabrics UD (425 g/m2)
- Laminate thickness = 3.1 - 3.25 min
- Fibre volume content: 59 - 63 %
- Cure: 1 h 80 °C + 4 h 120°C
Safety & Health
- First Aid Information
- Contamination of the eyes by resin, hardener or mix should be treated immediately by flushing with clean, running water for 10 to 15 minutes.
- A doctor should then be consulted. Material smeared or splashed on the skin should be dabbed off, and the contaminated area then washed and treated with a cleansing cream (see above). A doctor should be consulted in the event of severe irritation or burns.
- Contaminated clothing should be changed immediately. Anyone taken ill after inhaling vapours should be moved out of doors immediately. In all cases of doubt call for medical assistance.
Storage & Handling
- Storage Conditions
- Provided that Araldite® LY 1564 and Aradur® 3474 are stored in a dry place in their original, properly closed containers at the above mentioned storage temperatures they will have the shelf lives indicated on the labels.
- Partly emptied containers should be closed immediately after use.
- Handling Information
Safety Precautions Protective clothing Yes Gloves Essential Arm protectors Recommended when skin contact likely
Goggles/safety glasses Yes Respirator/dust mask Recommended Skin Protection Skin protection before starting Apply barrier cream to exposed skin
Skin protection after washing Apply barrier or nourishing cream
Cleansing of contaminated skin Dab off with absorbent paper, wash with warm water and alkali-free soap, then dry with disposable towels. Do not use solvents
Clean shop requirements Cover workbenches, etc. with light coloured paper. Use disposable breakers, etc.
Disposal of spillage Soak up with sawdust or cotton waste and deposit in plastic-lined bin
Ventilation Ventilation of workshop Renew air 3 to 5 times an hour
Ventilation of workplace Exhaust fans. Operatives should avoid inhaling vapours.