- The system exhibits excellent mechanical properties and good thermal resistance
- Due to its high reactivity short cure cycles can be realized
Applications & Uses
- Composites Processing Methods
- Cure Method
- Product End Uses
- Processing Information
- Resin Transfer Moulding (RTM)
- Wet lay-up
- Pressure moulding
Properties
- Physical Form
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Processing Guidelines
Components Parts by weight Parts by volume Araldite® LY 1564 100 100 Aradur® 5003-1 19 23 - We recommend that the components are weighed with an accurate balance to prevent mixing inaccuracies which can affect the properties of the matrix system. The components should be mixed thoroughly to ensure homogeneity. It is important that the side and the bottom of the vessel are incorporated into the mixing process.
- When processing large quantities of mixture the pot life will decrease due to exothermic reaction. It is advisable to divide large mixes into several smaller containers.
- Properties of the Cured, Neat Formulation
Property Value Unit Test Method At Condition Glass Transition Temperature 50 - 56 °C ISO 11357-2, DSC 3 days 23°C Glass Transition Temperature 76 - 82 °C ISO 11357-2, DSC 4h 60°C Glass Transition Temperature 88 - 95 °C ISO 11357-2, DSC 30 min 80°C Glass Transition Temperature 95 - 102 °C ISO 11357-2, DSC 2h 80°C Glass Transition Temperature 96 - 105 °C ISO 11357-2, DSC 10 min 100°C Glass Transition Temperature 105 - 112 °C ISO 11357-2, DSC 1h 100°C Glass Transition Temperature 108 - 115 °C ISO 11357-2, DSC 30 min 80°C + 2h 120°C
Tensile Test Tensile strength 55 - 65 MPa ISO 527 30 min 80°C + 2h 120°C
Tensile Test Elongation at tensile strength 2.8 – 3.8 % ISO 527 30 min 80°C + 2h 120°C
Tensile Test Ultimate strength 55 - 65 MPa ISO 527 30 min 80°C + 2h 120°C
Tensile Test Ultimate elongation 3 - 4 % ISO 527 30 min 80°C + 2h 120°C
Tensile Test Tensile modulus 2600 - 2900 MPa ISO 527 30 min 80°C + 2h 120°C
Flexural Test Flexural strength 108 - 118 MPa ISO 178 30 min 80°C + 2h 120°C
Flexural Test Elongation at flexural strength 6.0 – 7.5 % ISO 178 30 min 80°C + 2h 120°C
Flexural Test Ultimate strength 105 - 115 MPa ISO 178 30 min 80°C + 2h 120°C
Flexural Test Ultimate elongation 7 - 9 % ISO 178 30 min 80°C + 2h 120°C
Flexural Test Flexural modulus 2600 - 2900 MPa ISO 178 30 min 80°C + 2h 120°C
Flexural Test Flexural strength 115 - 125 MPa ISO 178 30 min 80°C + 2h 120°C
Flexural Test Elongation at flexural strength 5 - 7 % ISO 178 30 min 80°C + 2h 120°C
Flexural Test Ultimate strength 110 - 120 MPa ISO 178 30 min 80°C + 2h 120°C
Flexural Test Ultimate elongation 6 - 9 % ISO 178 30 min 80°C + 2h 120°C
Flexural Test Flexural modulus 2800 - 3100 MPa ISO 178 30 min 80°C + 2h 120°C
Fracture Properties Fracture toughness K1C 0.9 - 1.0 MPa√m ISO 13586 30 min 80°C + 2h 120°C
Fracture Properties Fracture energy G1C 230 - 290 J/m² ISO 13586 30 min 80°C + 2h 120°C
Fracture Properties Fracture toughness K1C 0.8 - 0.9 MPa√m ISO 13586 30 min 80°C + 2h 120°C
Fracture Properties Fracture energy G1C 180 - 230 J/m² ISO 13586 30 min 80°C + 2h 120°C
- Properties of The Cured, Reinforced Formulation
Property Value Unit Test Method At Condition Shear Strength (LY 1564 Ar. 5003-1) 52 - 56 MPa ASTM D 2344 30 min 80°C + 20 min 120°C
Shear Strength (LY 3585 Ar. 5003-1) 62 - 67 MPa ASTM D 2344 30 min 80°C + 20 min 120°C
Note
- Short beam: Laminate comprising 12 layers unidirectional
- E-glass fabric (425 g/m²)
- Laminate thickness t = 3.0 - 3.2 mm
- Fibre volume content: 63 - 65 %
- Properties of the Cured, Reinforced Formulation
Property Value Unit Test Method At Condition Shear Strength (LY 1564 Ar. 5003-1) 52 - 56 MPa ASTM D 2344 30 min 80°C + 20 min 120°C
Shear Strength (LY 3585 Ar. 5003-1) 62 - 67 MPa ASTM D 2344 30 min 80°C + 20 min 120°C
Note
- Short beam: Laminate comprising 12 layers unidirectional
- E-glass fabric (425 g/m²)
- Laminate thickness t = 3.0 - 3.2 mm
- Fibre volume content: 63 - 65 %
Safety & Health
- First Aid Information
- Contamination of the eyes by resin, hardener or mix should be treated immediately by flushing with clean, running water for 10 to 15 minutes.
- A doctor should then be consulted. Material smeared or splashed on the skin should be dabbed off, and the contaminated area then washed and treated with a cleansing cream (see above).
- A doctor should be consulted in the event of severe irritation or burns. Contaminated clothing should be changed immediately.
- Anyone taken ill after inhaling vapours should be moved out of doors immediately. In all cases of doubt call for medical assistance.
Storage & Handling
- Storage Conditions
- Provided that Araldite® LY 1564, Araldite® LY 3585 or Aradur® 5003-1 are stored in a dry place in their original, properly closed containers at the storage temperatures mentioned in the MSDS they will have the shelf lives indicated on the labels.
- Partly emptied containers should be closed immediately after use.
- Araldite® LY 3585 which has crystallized and looks cloudy can be restored to its original state by heating to 60 - 80°C.
- Handling Information
Safety Precautions Protective clothing Yes Gloves Essential Arm protectors Recommended when skin contact likely
Goggles/safety glasses Yes Respirator/dust mask Recommended Skin Protection Skin protection before starting Apply barrier cream to exposed skin
Skin protection after washing Apply barrier or nourishing cream
Cleansing of contaminated skin Dab off with absorbent paper, wash with warm water and alkali-free soap, then dry with disposable towels. Do not use solvents
Clean shop requirements Cover workbenches, etc. with light coloured paper. Use disposable breakers, etc.
Disposal of spillage Soak up with sawdust or cotton waste and deposit in plastic-lined bin
Ventilation Ventilation of workshop Renew air 3 to 5 times an hour
Ventilation of workplace Exhaust fans. Operatives should avoid inhaling vapours.