Enhanced TDS
Identification & Functionality
- Blend
- No
- Chemical Family
- Polymer Name
- Single Ingredient
- Yes
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Markets
- Applications
- Application Information
- Thin wall technical parts, thick wall extrusion profiles, spiral hoses, cable jacketing and film and sheet.
- Application Information
Thin wall technical parts, thick wall extrusion profiles, spiral hoses, cable jacketing and film and sheet.
- Material Preparation
Irogran® A 80 P 5039 is supplied pre-dried, however to ensure trouble-free processing it is preferable to dry before use. The recommended drying conditions are:
- 3 hours at 80-90°C in circulating air
- 3 hours at 70-80°C in dehumidified air
- Dew point: -30°C
Properties
- Physical Form
- Notes
* - Mold shrinkage is dependent on wall thickness and processing parameters.
Regulatory & Compliance
Technical Details & Test Data
- Material Preparation
- IROGRAN® A 80 P 5039 is supplied pre-dried, however to ensure trouble-free processing it is preferable to dry before use.
- The recommended drying conditions are:
- 3 hours at 80-90°C in circulating air
- 3 hours at 70-80°C in dehumidified air
- Dew point: -30°C
Safety & Health
- Health & Safety Advice
- Before undertaking any trials with this product it is essential that all personnel are aware of the necessary precautions that must be taken.
Packaging & Availability
Storage & Handling
- Storage Information
Irogran® A 80 P 5039 has a minimum expected shelf life of 12 months after shipment date. The product should be stored in a dry and cool place in the manufacturer ́s original packaging.
- Storage Information
- IROGRAN® A 80 P 5039 is supplied in bags, drums or octabins.
- IROGRAN® A 80 P 5039 has a minimum expected shelf life of 12 months after shipment date.
- The product should be stored in a dry and cool place in the manufacturer ́s original packaging.
Other
- Appearance (SDS)
- Pellets
- Mechanical Properties
Value Units Test Method / Conditions Compression Set 27.0 % % ASTM D395 at 23°C, 22 hrs Compression Set 80.0 % % ASTM D395 at 70°C 22 hrs Hardness 81.0 Shore A Shore A ASTM D2240 3 seconds Hardness 33.0 Shore D Shore D ASTM D2240 after 3 seconds Tear Strength 380.0 PLI PLI ASTM D624 Tensile Strength 5660.0 psi psi ASTM D412 at break - Physical Properties
Value Units Test Method / Conditions Density 1.1 g/cm³ g/cm³ ASTM D792 Glass Transition Temperature (Tg) -40.0 °C °C ASTM D3418 Melting Point 145.0-155.0 °C °C