Enhanced TDS
Identification & Functionality
- CASE Ingredients Functions
- Chemical Family
- Technologies
- Product Families
Features & Benefits
- CASE Ingredients Features
- Features Information
- Room temperature cure
- Long pot life with short tack-free times
- Superior corrosion resistance
Applications & Uses
- Coating End Applications
- Compatible Polymers & Resins
- Markets
- Applications
- Application Information
- Chemical resistant coatings
- Adhesives
- Maintenance coating
- Primers
- Enamel paint formulations
Properties
- Physical Form
Regulatory & Compliance
Technical Details & Test Data
- Processing Information
Mix ratio with 190 EEW solid epoxy is 104 phr. Due to chemical reaction, VERSAMID® 115 and epoxy resins should not be mixed until just prior to use.
Typical Chemical Resistance Properties (21 Day Immersion at 25°C)Chemical % Weight Gain 10% Acetic acid 12.40% 10% Hydrochloric acid 1.90% 10% Sulfuric acid 3.20% 10% Sodium Hydroxide 0.60% Methyl ethyl ketone Destroyed Xylene Destroyed Ethanol 13.50% Typical Properties of a VERSAMID® 115 Cured Coating
Property Value Tack Free Time 4.3 hours Through-cure time 6 hours Pot Life 4 hours Tensile Strength 6000 psi Elongation 8 % Flexural Modulus 320 kpsi Tg 62 °C max
Packaging & Availability
- Regional Availability
Storage & Handling
- Storage Information
- VERSAMID® 115 should be stored in a dry place, in its sealed original container, at temperatures between 2°C to 40°C (35.6°F to 104°F).
- Under these storage conditions the shelf life is 24 months from date of manufacture. The product should not be exposed to direct sunlight.
Other
- Appearance (SDS)
- Liquid
- Color (SDS)
- Amber
- Odor (SDS)
- Ammoniacal
- Chemical Properties
Value Units Test Method / Conditions Amine Hydrogen Equivalent Weight 198.0 AHEW AHEW Amine Value 230.0-246.0 mg KOH/g mg KOH/g - Physical Properties
Value Units Test Method / Conditions Density 8.1 lb/gal lb/gal Flash Point min. 200.0 °F °F SETA Viscosity 3500.0-4500.0 cPs cPs Brookfield Viscometer at 75°C - Application Information
Value Units Test Method / Conditions Mix Ratio 105.0 phr phr with bis A epoxy resin