Enhanced TDS
Identification & Functionality
- Chemical Family
- RTU Product Type
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
- Key Properties
- Good mechanical and electrical properties
- High Toughness
- Suited for Class A (105 °C) - applications
Applications & Uses
- Composites Processing Methods
- Cure Method
- Product End Uses
- Processing Methods
Casting, with and without applying vacuum
- Application Information
Encapsulation of electronic devices (esp. PWB's)
Properties
- Physical Form
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Cured Properties
Key Value Unit Test Method Test Condition Glass transition temperature (Tg) 95 - 100 °C IEC 1006, DSC, 10 K/MIN Cure: 4 h 80 °C + 4 h 120 °C
Tensile strength 88 - 95 MPa ISO 527 Cure: 4 h 80 °C + 4 h 120 °C
Elongation at tensile strength 5.0 - 6.0 % ISO 527 Cure: 4 h 80 °C + 4 h 120 °C
Ultimate strength 87 - 94 MPa ISO 527 Cure: 4 h 80 °C + 4 h 120 °C
Ultimate elongation 5.5 - 6.5 % ISO 527 Cure: 4 h 80 °C + 4 h 120 °C
Tensile modulus 3100 - 3200 MPa ISO 527 Cure: 4 h 80 °C + 4 h 120 °C
Flexural strength 150 - 155 MPa ISO 178 Cure: 4 h 80 °C + 4 h 120 °C
Elongation at flexural strength 6.5 - 7.0 % ISO 178 Cure: 4 h 80 °C + 4 h 120 °C
Ultimate strength 148 - 155 MPa ISO 178 Cure: 4 h 80 °C + 4 h 120 °C
Ultimate elongation 6.5 - 8.0 % ISO 178 Cure: 4 h 80 °C + 4 h 120 °C
Flexural modulus 3200 - 3350 MPa ISO 178 Cure: 4 h 80 °C + 4 h 120 °C
Fracture toughness K1C 0.57 - 0.60 MPa√m PM 258-0/90 Cure: 4 h 80 °C + 4 h 120 °C
Fracture energy G1C 110 - 120 J/m² PM 258-0/90 Cure: 4 h 80 °C + 4 h 120 °C
Water absorption 0.10 - 0.15 % ISO 62 Cure: 4 h 80 °C + 4 h 120 °C
Water absorption (10 days H₂O 23 °C) 0.35 - 0.40 % ISO 62 Cure: 4 h 80 °C + 4 h 120 °C
Water absorption (60 min H₂O 100 °C) 0.20 - 0.25 % ISO 62 Cure: 4 h 80 °C + 4 h 120 °C
Poisson's ratio 0.35 μ N/A N/A
Safety & Health
- First Aid
Contamination of the eyes by resin, hardener or casting mix should be treated immediately by flushing with clean, running water for 10 to 15 minutes. A doctor should then be consulted. Material smeared or splashed on the skin should be dabbed off, and the contaminated area then washed and treated with a cleansing cream. A doctor should be consulted in the event of severe irritation or burns. Contaminated clothing should be changed immediately. medical assistance. Anyone taken ill after inhaling vapours should be moved out of doors immediately. In all cases of doubt call for medical assistance
- Industrial Hygiene
Mandatory and recommended industrial hygiene procedures should be followed whenever our products are being landled and processed. For additional information please consult the corresponding Safety Data Sheets and the brochure "Hygienic precautions for handling plastics products of Vantico" (Publ. No. 24264/e).
Storage & Handling
- Storage Conditions
Store the components in tightly sealed and dry original containers (see labels on containers) . Under these conditions, the shelf life will correspond to the expiration date stated on the label. After this date, the product may e processed only following reanalysis. Partly emptied containers should be closed tightly immediately after use. For information on waste disposal and hazardous products of decomposition in the event of fire, refer to the Material Safety Data Sheets (MSDS) for these particular products.