- High strength
- Tough, heat resistant
- Features Information
- High strength
- Tough, heat resistant
Applications & Uses
- Compatible Substrates & Surfaces
- Markets
- Applications
Properties
- Physical Form
Technical Details & Test Data
- Technical Data
Typical physical properties:
Unless otherwise stated, the data were determined with typical production batches using standard test methods. They are typical values only, and do not constitute a product specification. Unless otherwise noted, tests were performed at 77°F (25°C).
Property Conditions Test Method Value Tensile lap shear, psi (MPa) at -55°C, aluminum, unconditioned ASTM D1002 3,000 (20.7) Tensile lap shear, psi (MPa) at 25°C, aluminum, unconditioned ASTM D1002 2,500 (17.2) Tensile lap shear, psi (MPa) at 121°C, aluminum, unconditioned ASTM D1002 900 (6.2) Cured 2h at 25°C + 1h at 100°C at 25°C ASTM D1002 4,700 (32.4) Cured 2h at 25°C + 1h at 100°C at 100°C ASTM D1002 1,300 (9.0) Cured 2h at 25°C + 1h at 100°C at 149°C ASTM D1002 300 (2.0) After 30 days at 63°C/95% RH at 25°C ASTM D1002 2,500 (17.2) After 30 days at 63°C/95% RH at 121°C ASTM D1002 700 (4.8) T-peel, Aluminum, pli (N/mm) Unconditioned ASTM D1876 35 (6.1) T-peel, Aluminum, pli (N/mm) After 30 days at 63°C/95% RH ASTM D1876 35 (6.1) Tear Resistance, lbf/in ASTM D624 (C) 290 Elongation, % ASTM D412 290 Durometer hardness, Shore D Unconditioned ASTM D2240 50 Durometer hardness, Shore D After 30 days at 63°C/95% RH 50 Tested after Thermal Aging Exposure:
Property Conditions Initial 100 hours 500 hours 1,000 hours Tensile lap shear, Al-Al, psi (MPa) at -55°C 5,500 (37.9) 6,500 (44.8) 6,400 (44.1) 5,500 (37.9) Tensile lap shear, Al-Al, psi (MPa) at 25°C 2,800 (19.3) 3,200 (22) 2,800 (19.3) 3,000 (20.6) Tensile lap shear, Al-Al, psi (MPa) at 121°C 950 (6.5) 1,000 (6.9) 1,000 (6.9) 950 (6.5) T-peel, pli (N/mm) at 25°C 60 (10.5) 90 (15.7) 90 (15.7) 80 (14) - Processing Information
Mix both components thoroughly for several minutes to insure uniform blending. Material temperatures should be above 18°C when mixing. Avoid air entrapment while mixing.
Processing data:
Parameter Value Gel time 25 - 45 min at 25°C, 50g Typical cure cycles 5 - 7 days at 23°C Typical cure cycles 1-2 hours at 25°C + 16 hours at 66°C
Typical cure cycles 2 hours at 25°C + 1 hour at 100°C
Safety & Health
- Safety Information
Keep out of reach of children
Packaging & Availability
- Packaging Type
- Regional Availability
Storage & Handling
- Storage Conditions
URALANE® 5773-A/B should be stored in a dry place, in the original sealed container at temperatures between 2°C and 40°C (36°F and 104°F). Under these storage conditions, and when supplied under Huntsman standard certification, the product has a shelf-life of 6 months from date of shipment (expiration date may differ based on customer specification). The product should not be exposed to direct sunlight. These products are moisture sensitive and are packaged under a blanket of dry nitrogen. After opening a container, re-blanket with dry nitrogen and then tightly reseal.
- Storage Information
- Uralane® 5773 A/B should be stored in a dry place, in the original sealed container at temperatures between 2°C and 40°C (36°F and 104°F).
- Under these storage conditions, and when supplied under Huntsman standard certification, the product has a shelf-life of 6 months from date of shipment (expiration date may differ based on customer specification).
- The product should not be exposed to direct sunlight.
- These products are moisture sensitive and are packaged under a blanket of dry nitrogen. After opening a container, re-blanket with dry nitrogen and then tightly reseal.
Other
- Appearance
- Dark amber
- Physical Properties
Value Units Test Method / Conditions Density 1.25 g/cm³ g/cm³ ASTM D792