Features & Benefits
- Ready-to-Use Product Features
- Key Features
- Non-structural adhesive
- Long work life
- Room temperature cure
Applications & Uses
- Application Method
- Compatible Substrates & Surfaces
- Markets
- Applications
Properties
- Physical Form
Regulatory & Compliance
- OEM Specifications
Technical Details & Test Data
- Technical Data
Typical physical properties
Unless otherwise stated, the data were determined with typical production batches using standard test methods. They are typical values only, and do not constitute a product specification.
Property
Test Method
Value
Lap Shear Strength, Al-Al, psi (MPa) -65°F (-55°C) ASTM D1002 2,800 psi (19.3 MPa)
Lap Shear Strength, Al-Al, psi (MPa) 77°F (25°C) ASTM D1002 2,500 psi (17.2 MPa)
Lap Shear Strength, Al-Al, psi (MPa) 180°F (82°C) ASTM D1002 800 psi (5.5 MPa)
Tg (DMA), °F (°C) E’ Onset Huntsman 165°F (74°C) Tg (DMA), °F (°C) Tan δ peak Huntsman 212°F (100°C) CTE (TMA), ppm/°C α1: Below transition Huntsman 80 CTE (TMA), ppm/°C α2: Above transition Huntsman 206.9 Thermal Conductivity, W/mK C-Therm TCi 0.4 Hardness, Shore D ASTM D2240 80 - Processing Information
Material temperatures should be above 65°F (18°C) when mixing. Mix both components thoroughly for several minutes to insure complete and uniform mixing.
Parameter Value Work life, 100g at 25°C 3 - 4 hours Typical cure cycles
48 hours at 23 - 26°C
Gel at RT + 1 hour at 93°C
Storage & Handling
- Storage Conditions
EPIBOND® 1210 A-1 / 9615-10 should be stored in a dry place in the original sealed containers at temperatures between 2°C and 40°C (36°F and 104°F). After use, tightly reseal containers. Under these storage conditions, and when supplied under Huntsman standard certification, the product has a shelf life of 1 year from date of shipment. The product should not be exposed to direct sunlight.
Other
- Appearance
- Grey blue
- Thermal Properties
Value Units Test Method / Conditions Thermal Conductivity 0.4 W/m·K W/m·K C-Therm TCi - Mechanical Properties
Value Units Test Method / Conditions Hardness 80.0 Shore D Shore D ASTM D2240 - Physical Properties
Value Units Test Method / Conditions Density 1.3 g/cm³ g/cm³ ASTM D792 at 25°C Glass Transition Temperature (Tg) 74.0 °C °C Dynamic Mechanical Analysis (DMA) E' Onset Glass Transition Temperature (Tg) 100.0 °C °C Dynamic Mechanical Analysis (DMA) Tan peak Lap Shear Strength 19.3 MPa MPa ASTM D1002 at -55°C, Al-Al - Application Information
Value Units Test Method / Conditions Curing Time 48.0 hr hr at 23 - 26°C