Enhanced TDS
Identification & Functionality
- Chemical Family
- Function
- 1K (1 component) Adhesive,2K (2 component) Filler,Syntactic Adhesive
- RTU Product Type
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
- Product Feature
- General purpose adhesive
- Room temperature cure
- Product Features
- General purpose adhesive
- Room temperature cure
Applications & Uses
- Application Area
- Application Method
- Compatible Substrates & Surfaces
- Markets
- Applications
- Mixing Ratio
Product Parts by weight EPIBOND® 1210 A-1 Resin 100 Hardener 9615 A 65 Material temperatures should be above 65°F (18°C) when mixing. Mix both components thoroughly for several minutes to insure complete and uniform mixing.
Properties
- Physical Form
Regulatory & Compliance
- Chemical Inventories
- OEM Specifications
Technical Details & Test Data
- Guideline Values
Property Value Unit Test Method Condition Maximum Service Temperature 93 °C ASTM D648 Tensile Lap Shear 2,500 psi ASTM D1002 Al-Al at 25°C (cured 25°C / 2 days)
Tensile Lap Shear 3,100 psi ASTM D1002 Al-Al at 25°C (cured 25°C / 2h + 121C/ 30min)
Tensile Lap Shear 525 psi ASTM D1002 Al-Al at 150°C Tensile Lap Shear 1,800 psi ASTM D1002 Steel to steel at 25°C
Tensile Lap Shear 1,500 psi ASTM D1002 polyester to polyester at 25°C
Fluid Immersion 2,000 psi ASTM D1002 JP-4, 7 days at 23°C
Fluid Immersion 2,000 psi ASTM D1002 Skydrol, 7 days at 23°C
Fluid Immersion 2,300 psi ASTM D1002 Distilllled water, 7 days at 23°C
Coefficient of Thermal Expansion 73.5 ppm/°C Huntsman, Thermomechanical Analysis α1: Below transition
Coefficient of Thermal Expansion 132.4 ppm/°C Huntsman, Thermomechanical Analysis α2: Above transition
Thermal Conductivity 0.45 W/mK C-Therm TCi Heat Capacity 700 J/Kg/K C-Therm TCi Hardness 80 Shore D ASTM D2240 at 25°C - Processing Information
Processing Guidelines
Material temperatures should be above 65°F (18°C) when mixing. Mix both components thoroughly for several minutes to insure complete and uniform mixing.
Parameter
Value
Work life, 100g at 25°C, min 50 - 75 Typical cure cycles 48 hours at 23 - 26°C or
3 hours at 66°C Guideline Values
Property
Value
Unit
Test Method
Condition
Maximum Service Temperature 93 °C ASTM D648 Tensile Lap Shear 2,500 psi ASTM D1002 Al-Al at 25°C (cured 25°C / 2 days)
Tensile Lap Shear 3,100 psi ASTM D1002 Al-Al at 25°C (cured 25°C / 2h + 121C/ 30min)
Tensile Lap Shear 525 psi ASTM D1002 Al-Al at 150°C Tensile Lap Shear 1,800 psi ASTM D1002 Steel to steel at 25°C
Tensile Lap Shear 1,500 psi ASTM D1002 polyester to polyester at 25°C
Fluid Immersion 2,000 psi ASTM D1002 JP-4, 7 days at 23°C
Fluid Immersion 2,000 psi ASTM D1002 Skydrol, 7 days at 23°C
Fluid Immersion 2,300 psi ASTM D1002 Distilllled water, 7 days at 23°C
Coefficient of Thermal Expansion 73.5 ppm/°C Huntsman, Thermomechanical Analysis α1: Below transition
Coefficient of Thermal Expansion 132.4 ppm/°C Huntsman, Thermomechanical Analysis α2: Above transition
Thermal Conductivity 0.45 W/mK C-Therm TCi Heat Capacity 700 J/Kg/K C-Therm TCi Hardness 80 Shore D ASTM D2240 at 25°C
Packaging & Availability
- Regional Availability
Storage & Handling
- Storage Conditions
- EPIBOND® 1210 A-1/9615 A should be stored in a dry place in the original sealed containers at temperatures between 2°C and 40°C.
- After use, tightly reseal containers.
- Under these storage conditions, and when supplied under Huntsman standard certification, the product has a shelf life of 1 year (from date of shipment).
- The product should not be exposed to direct sunlight.
- Storage Information
EPIBOND® 1210 A-1 / 9615 A should be stored in a dry place in the original sealed containers at temperatures between 2°C and 40°C (36°F and 104°F). After use, tightly reseal containers.
Other
- Physical Properties
Value Units Test Method / Conditions Density 1.3 g/cm³ g/cm³ ASTM D792 at 25°C