Enhanced TDS
Identification & Functionality
- Chemical Family
- RTU Product Type
- Technologies
- Product Families
Features & Benefits
- Ready-to-Use Product Features
- Product Advantages
- Excellent flexibility
- Convenient mix ratio
- Bonds a wide variety of materials
- Rapid cure time
Applications & Uses
- Compatible Substrates & Surfaces
- Applications
- Polycarbonate
- ABS
- Nylon
- Metton
- Vulcanized rubber
- Primed metals
Technical Details & Test Data
- Cured Properties
Standard Test Specimens
Unless otherwise stated, the figures given below were all determined by testing standard specimens made up by lap-jointing 4-inch x 1-inch x 0.06-inch (10-cm x 2.5-cm x 1.5-mm) strips of aluminum. The joint area was 0.5 x 1 inch (12.5 mm x 2.5 cm) in each case.
Property
Value(1)
Unit
Test Method
at Condition
Lap Shear Strength 1450 (10) psi (MPa) ASTM D-1002 Substrate: Aluminum, Cured 20 min at 212°F (100°C)
Lap Shear Strength 800 (5.5) psi (MPa) ASTM D-1002 Substrate: Metton®, Cured 20 min at 212°F (100°C)
Hardness 85 Shore D ASTM D-2240 - Ultimate Tensile Strength 2100 (14.5) psi (MPa) ASTM D-638 - Elongation, % 250 % ASTM D-638 - Tg per DMA 86 (30) °F (°C) ASTM E-831 - Coefficient of Thermal Expansion 13.5 x 10⁻⁵ (2) in/in/°C ASTM D-4065 Below Tg Coefficient of Thermal Expansion 23 x 10⁻⁵ (3) in/in/°C ASTM D-4065 Above Tg Note - (1)Tested @ 77 °F (25℃)
Safety & Health
- Safety Information
- Eyes and skin : Flush eyes with water for 15 minutes. Contact a physician if irritation persists. Wash skin thoroughly with soap and water. Remove and wash contaminated clothing before reuse.
- Inhalation : Remove subject to fresh air.
- Swallowing : Dilute by giving water to drink and contact a physician promptly. Never give anything to drink to an unconscious person.
Other
- Physical Properties
Value Units Test Method / Conditions Viscosity 50000.0 cPs cPs ASTM D2393 at 25°C